The Dynamics of Surface Alloys: Rearrangement of Pd/Ag(111) Induced by CO and O2

Citation:

van Spronsen MA, Duanmu K, O'Connor CR, Egle T, Kersell H, Oliver-Meseguer J, Salmeron M, Madix RJ, Sautet P, Friend CM. The Dynamics of Surface Alloys: Rearrangement of Pd/Ag(111) Induced by CO and O2. Journal of Physical Chemistry C. 2018;(part of the Hans-Joachim Freund and Joachim Sauer Festschrift special issue).

Abstract:

Alloys of Ag and small amounts of Pd are promising as bifunctional catalysts, potentially combining the inherent selectivity of the noble Ag with that of the more reactive Pd. Stable PdAg surface alloys are prepared via evaporation of Pd onto Ag(111) at room temperature followed by annealing at 400 K to create a model system. Using this procedure, the most stable form of the surface alloy under vacuum was determined to be a Ag-capped PdAg surface alloy, on the basis of a combination of X-ray photoelectron spectroscopy (XPS), scanning tunneling microscopy (STM), and density functional theory (DFT). Extensive roughening of the surface was apparent in STM images, characterized by islands of the Ag/PdAg/Ag(111) alloy of several layers thickness. The roughening is attributed to transport of Ag from the Ag(111) surface into the alloy islands. Within these islands, there is a driving force for Pd to be dispersed, surrounded by Ag, on the basis of DFT modeling. Exposure of these Ag/PdAg/Ag(111) islands to CO (0.5 Torr) at 300 K induces migration of Pd to the surface, driven by the energetic stabilization of the Pd–CO bond based on ambient-pressure XPS. Once the Pd is drawn to the surface by higher pressures of CO at room temperature, it remains stable even under very low CO partial pressures at temperatures of 300 K and below, on the basis of DFT-modeled phase behavior. Exposure to 1 Torr of O2 at 400 K also causes Pd to resurface, and the resulting structure persists even at low pressures and temperatures below 300 K. These results establish that the state of the PdAg catalyst surface depends strongly on pretreatment and operational conditions. Hence, exposure of an alloy catalyst to CO or O2 at moderate temperatures and pressures can lead to catalyst activation by bringing Pd to the surface. Furthermore, these results demonstrate that exposure to CO at room temperature, which is often used as a proxy for evaluating the Pd coordination sites available in a catalyst, changes the surface structure. Therefore, the CO vibrational frequencies measured with diffuse-reflectance infrared Fourier-transform spectroscopy (DRIFTS) on PdAg catalyst materials do not necessarily provide information about their working state, and fundamental understanding of the CO-PdAg alloy is crucial.

Publisher's Version